Analisis kegagalan penipisan dinding pipa pada bagian economizer ketel uap pipa air
Info Katalog
File Repositori
Subyek : Pipe - Sizes;Pipe - Standards
Penerbit : FTI - Usakti
Kota Terbit : Jakarta
Tahun Terbit : 2014
Pembimbing 1 : Dody Prayitno
Kata Kunci : boiler, creep
Status Posting : Published
Status : Tidak Lengkap
File Repositori
| No. | Nama File | Hal. | Link |
|---|---|---|---|
| 1. | 2014_TS_MTM_161111001_Halaman-Judul.pdf | ||
| 2. | 2014_TS_MTM_161111001_Lembar-Pengesahan.pdf | ||
| 3. | 2014_TS_MTM_161111001_Bab-1_Pendahuluan.pdf | ||
| 4. | 2014_TS_MTM_161111001_Bab-2_Tinjauan-Pustaka.pdf |
|
|
| 5. | 2014_TS_MTM_161111001_Bab-3_Metodologi-Penelitian.pdf |
|
|
| 6. | 2014_TS_MTM_161111001_Bab-4_Analisis-dan-Pembahasan.pdf |
|
|
| 7. | 2014_TS_MTM_161111001_Bab-5_Kesimpulan-dan-Saran.pdf |
|
|
| 8. | 2014_TS_MTM_161111001_Daftar-Pustaka.pdf | ||
| 9. | 2014_TS_MTM_161111001_Lampiran.pdf |
|
P Pada tahun 2008 pipa standar pada bagian economizer ketel uap pipa air buatan Kvaerner Finlandia telah diganti dengan pipa galvanis. Pipa galvanis pada 2013 ditemukan menipis. Setelah beroperasi sekitar 5 tahun, ketebalan pipa galvanis lebih tipis dari sebelumnya. Tujuan penelitian adalah untuk menganalisis kegagalan mengapa ketebalan pipa menipis. Metodologi penelitian adalah pengukuran diameter, pengukuran ketebalan, uji kekerasan, uji metalografi, dan pengujian komposisi kimia. Hasilnya penelitian ini menunjukkan bahwa penipisan pipa galvanis disebabkan oleh creep. Suh di dalam dan luar sisi pipa berbeda. Suhu di luar pipa lebih tinggi dari pada dalam. Ada tekanan fluida di dalam pipa. Tekanan dan suhu fluida konstan selama 5 tahun. Tekanan menyebabkan deformasi pada pipa. Dengan demikian diameter dalam pipa membesar sehingga dinding pipa menjadi lebih tipis. Deformasi dinding disebabkan oleh hialsmeningkatnya microcrack
A At 2008 a standard pipe at economizer boiler water tube made in Kvaerner Finland has replaced by galvanis pipe. The galvanis pipe at 2013 was found thinned After operated around 5 years, the thickness of galvanis pipe was thinner than before. The purpose of reseach are to analyzed the failure why the thickness of the pipe was thinning. The methodology reseach are diameter measurement, thickness measurement, hardness testing, metalography testing, and chemical composition testing The result this reseach show that thinning of galvanis pipe caused by creep. Temperature inside and out side of the pipe are different. The outside pipe temperature is higher than the inside. There is a pressure of fluid inside the pipe. The pressure and temperature offluid are constant for 5 year. The pressure cause deformation at the pipe. Thus the inside diameter of pipe become larger and make the thick of pipe wall become thinner. The deformation of wall is cause by increasing of microcrack.