Karakterisasi paduan logam amorf Zr60Cu25Ni5Al10 yang dibuat dengan metode arc melting, induction melting dan water quenching
Info Katalog
File Repositori
Subyek : Amorphous substances;Alloys
Penerbit : FTI - Usakti
Kota Terbit : Jakarta
Tahun Terbit : 2021
Pembimbing 1 : Triyono
Pembimbing 2 : Daisman P.B.Aji
Kata Kunci : amorphous alloy, water quenching, sem; eds, phase transformation
Status Posting : Published
Status : Tidak Lengkap
File Repositori
| No. | Nama File | Hal. | Link |
|---|---|---|---|
| 1. | 2021_TS_MTM_161170005_Halaman-Judul.pdf | ||
| 2. | 2021_TS_MTM_161170005_Lembar-Pengesahan.pdf | ||
| 3. | 2021_TS_MTM_161170005_Bab-1_Pendahuluan.pdf | ||
| 4. | 2021_TS_MTM_161170005_Bab-2_Tinjauan-Pustaka.pdf |
|
|
| 5. | 2021_TS_MTM_161170005_Bab-3_Metodologi-Penelitian.pdf |
|
|
| 6. | 2021_TS_MTM_161170005_Bab-4_Analisis-dan-Pembahasan.pdf |
|
|
| 7. | 2021_TS_MTM_161170005_Bab-5_Kesimpulan.pdf |
|
|
| 8. | 2021_TS_MTM_161170005_Daftar-Pustaka.pdf |
K Karakterisasi Paduan Logam Amorf Zr60Cu25Ni5Al10 yangdibuat dengan Metode Arc Melting, Induction Melting, dan Water Quenching salah satu metode untuk membuat paduan logam lebih keras, lebih kuat, dan lebihrendah dalam kapasitas redaman adalah dengan memanipulasi struktur atompaduan menjadi amorf. Studi ini melaporkan pembuatan paduan amorf dengankomposisi Zr60Cu25Ni5Al10 (at%). Paduan itu dibuat dengan pendinginan air(water quenching) dari lelehan induksi busur-mencair ingot (arc-melted ingot).Difraksi sinar-X menunjukkan bahwa spesimen sepenuhnya amorf danpengukuran Differential Scanning Calorimetry (DSC) menunjukkan suhu transisigelas, Tg, 417 oC dan suhu kristalisasi awal, Tx, 485 oC. Gambar ScanningElectron Microscopy (SEM) menunjukkan permukaan amorf fitur non-kristal danhasil analisis Energy Dispersive Spectroscopy (EDS) menunjukkan komposisinominal Zr60Cu25Ni5Al10. Fase kristal untuk sampel yang terkristalisasi yang dapatdiidentifikasi adalah Zr2Cu dan Zr2Ni.
C Characterization of Zr60Cu25Ni5Al10 Amorphous Metal AlloyPrepared by Arc Melting, Induction Melting, and WaterQuenching.One method to make a metallic alloy harder, stronger and lower in dampingcapacity is by making the atomic structure of the alloy into amorphous structure.This thesis reports a fabrication of a bulk amorphous alloy with a composition ofZr60Cu25Ni5Al10 (at%). The alloy was fabricated by water quenching the inductionmelt of an arc-melted ingot. X-rays diffraction (XRD) shows that the specimen isfully amorphous and Differential Scanning Calorimetry (DSC) measurementsshows glass transition temperature, Tg, of 417 oC and onset crystallizationtemperature, Tx, of 485 oC. SEM image shows the amorphous surface of noncrystalline feature and Energy Dispersive Spectroscopy (EDS) analysis reveals thenominal composition of Zr60Cu25Ni5Al10. After crystallization the samples, thecrystalline phases that could be identified were Zr2Cu and Zr2Ni.