Karakteristik kekuatan mekanik beton terhadap penambahan crumb rubber dan fly ash


Oleh : Dina Ativah

Info Katalog

Penerbit : FTSP - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2022

Pembimbing 1 : Liana Herlina

Subyek : Concrete - Construction

Kata Kunci : compressive strength and modulus of elasticity, shear strength, flexural strength


File Repositori
No. Nama File Ukuran (KB) Status
1. 2022_TA_STS_051001600025_-Halaman-Judul.pdf 12601.43
2. 2022_TA_STS_051001600025_Lembar-Pengesahan.pdf 1797.33
3. 2022_TA_STS_051001600025_Bab-1_Pendahuluan.pdf 1360.38
4. 2022_TA_STS_051001600025_Bab-2_Tinjauan-Pustaka.pdf 2948.12
5. 2022_TA_STS_051001600025_Bab-3_Metodologi-Penelitian.pdf 3299.52
6. 2022_TA_STS_051001600025_Bab-4_Analisis-dan-Pembahasan.pdf 3364.51
7. 2022_TA_STS_051001600025_Bab-5_Kesimpulan.pdf 1744.59
8. 2022_TA_STS_051001600025_Daftar-Pustaka.pdf 1945.65
9. 2022_TA_STS_05100160025_lampiran.pdf 7630.22
10. 2022_TA_STS_051001600025_PPT-TA.pptx 8450.07
11. 2022_TA_STS_051001600025_Poster-TA.pdf 1933.88

L Limbah karet di Indonesia terus meningkat seiring dengan kebutuhan dan perkembangan teknologi. Pemanfaatan limbah karet pada daerah Kota Bima, Provinsi NTB masih sangat terbatas. Begitupun dengan limbah fly ash pada daerah lombok barat, Provinsi NTB sangat berlimpah. Disisi lain kebutuhan material beton sebagai bahan struktur terus berkembang dengan pesat untuk berbagai macam penggunaan. Sehingga perlu dilakukan upaya pemanfaatan penggunaan limbah fly ash dan limbah ban karet untuk pekerjaan konstruksi beton.Berkaitan dengan ini, diadakan penelitian yang menggunakan crumb rubber sebagai pengganti sebagaian pasir dengan proporsi crum rubber yang digunakan yaitu 0%, 5%, 10% dan 15% dan memanfaatkan fly ash dengan proporsi 15%. Kuat desain beton yang direncanakan adalah 30 MPa. Hasil penelitian menunjukkan bahwa kuat tekan terjadi penurunan sebesar 27,24%, seiring bertambahnya campuran crumb rubber. Begitupun dengan modulus elastisitas penurunan terjadi sebesar 25,41% sedangkan kuat geser terjadi penurunan sebesar 32,16%. Namun pada hasil pengujian kuat lentur mengalami peningkatan sebesar 2,37% dan 6,36% seiring di tambahkan nya variasi proporsi crumb rubber, dengan hasil nilai yang dicapai proporsi crumb rubber 10% sebesar 6,33 MPa dan proporsi crumb rubber 15% sebesar 6,60 MPa pengujian pada umur 28 hari.

R Rubber waste in Indonesia continues to increase in line with the needs and technological developments. Utilization of rubber waste in the area of Bima City, NTB Province is still very limited. Likewise with fly ash waste in the West Lombok area, NTB Province is very abundant. On the other hand, the need for concrete as a structural material continues to grow rapidly for various uses. So it is necessary to make efforts to utilize fly ash waste and rubber tire waste for concrete construction work.In this regard, a study was conducted using crumb rubber as a partial substitute for sand with the proportions of crum rubber used being 0%, 5%, 10% and 15% and using fly ash with a proportion of 15%. The design strength of the planned concrete is 30 MPa. The results showed that the compressive strength decreased by 27.24%, as the mixture of crumb rubber increased. Likewise, the modulus of elasticity decreased by 25.41% while the shear strength decreased by 32.16%. However, the results of the flexural strength test increased by 2.37% and 6.36% along with the addition of variations in the proportion of crumb rubber, with the results achieved that the 10% crumb rubber proportion was 6.33 MPa and the 15% crumb rubber proportion was 6 ,60 MPa testing at the age of 28 days.