Efektivitas teknik air abrasion pada preparasi gigi terhadap kekuatan ikatan resin komposit (scoping Review) (laporan penelitian)


Oleh : Cinantya Putri Parahita

Info Katalog

Nomor Panggil : 617.634 2 CIN e

Penerbit : FKG - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2021

Pembimbing 1 : drg. Ade Prijanti Dwisaptarini, Sp.KG.

Subyek : Dentistry;Dental - Technique

Kata Kunci : air abrasion, bond strength, composite resin, dentin, enamel, minimal intervention dentistry


File Repositori
No. Nama File Ukuran (KB) Status
1. 2021_TA_KG_040001700039_Halaman-judul.pdf 323.17
2. 2021_TA_KG_040001700039_Lembar-pengesahan.pdf 660.06
3. 2021_TA_KG_040001700039_Bab-1-Pendahuluan.pdf 199.24
4. 2021_TA_KG_040001700039_Bab-2-Tinjauan-pustaka.pdf 1031.64
5. 2021_TA_KG_040001700039_Bab-3-Kerangka-teori.pdf 184.8
6. 2021_TA_KG_040001700039_Bab-4-Metode-penelitian.pdf 242.34
7. 2021_TA_KG_040001700039_Bab-5-Hasil-penelitian.pdf 905.93
8. 2021_TA_KG_040001700039_Bab-6-Pembahasan.pdf 192.91
9. 2021_TA_KG_040001700039_Bab-7-Kesimpulan-dan-saran.pdf 166.21
10. 2021_TA_KG_040001700039_Daftar-pustaka.pdf 198.64
11. 2021_TA_KG_040001700039_Lampiran.pdf 1070.71

I Intervensi minimal kedokteran gigi merupakan konsep yang mengintegrasikan filosofi pencegahan, remineralisasi dan intervensi minimal. Salah satu teknik dari konsep ini adalah air abrasion. Tujuan: Untuk mengetahui efektivitas teknik air abrasion pada preparasi karies terhadap kekuatan ikat resin komposit dengan metode scoping review. Metode: Penelitian dilakukan menggunakan diagram PRISMA dengan database PubMed, PMC dan Elsevier dengan pencarian: ((("air abrasion" OR "air abraded") AND (composite OR "composite resin")) AND "bond strength"). Hasil: 14 artikel ditemukan sesuai dengan kriteria dan dibagi menjadi 5 kategori antara lain; uji teknik air abrasion dengan tipe bonding self-etch terhadap kekuatan tarik mikro, uji teknik air abrasion dengan tipe bonding total-etch terhadap kekuatan tarik mikro, uji teknik air abrasion dengan tipe bonding self-etch terhadap kekuatan tarik, uji teknik air abrasion dengan tipe bonding self-etch terhadap kekuatan geser, dan uji teknik air abrasion dengan tipe bonding total-etch terhadap kekuatan geser. Kesimpulan: Kategori hasil uji teknik air abrasion dengan tipe bonding self-etch terhadap kekuatan tarik mikro memiliki rata-rata dan standar deviasi 20.1 ± 5.3 - 71.7 ± 8.3 MPa; dengan tipe bonding total-etch 25.2 ± 7.2 MPa - 55.08 ± 3.74 MPa; dengan tipe bonding total-etch terhadap kekuatan tarik memiliki rata-rata dan standar deviasi 15.83 ± 1.51 - 20.80 ± 3.95 MPa; dengan tipe bonding self-etch terhadap kekuatan geser memiliki rata-rata dan standar deviasi 6.7 - 25.32 ± 4.91 MPa; dan dengan tipe bonding total-etch 13.88 ± 5.50 - 30.25 ± 7.00 MPa.

M Minimal intervention dentistry promote the philosophy of prevention, remineralization, and minimal invasive in the practice of dentistry. One of the technique employed by this concept is air abrasion. Aim: to discover the effectiveness of air abrasion technique on the dental caries prepation towards the bond strength of composite resin with the method of scoping review. Method: This research utilize the PRISMA diagram, based on PubMed, PMC and Elsevier database with the keywords of: ((("air abrasion" OR "air abraded") AND (composite OR "composite resin")) AND "bond strength"). Result: Based on the criteria, 14 were found and divided into 5 categories in which are; air abrasion technique with self-etch bonding type against microtensile bond strength test, air abrasion technique with total-etch bonding type against microtensile bond strength test, air abrasion technique with self-etch bonding type against tensile bond strength test, air abrasion technique with self-etch bonding type against shear bond strength test, air abrasion technique with total-etch bonding type against shear bond strength test. Conclusion: the mean and SD of air abrasion technique with self-etch bonding type against microtensile bond strength test is 20.1 ± 5.3 - 71.7 ± 8.3 MPa; with the total-etch bonding type is 25.2 ± 7.2 - 55.08 ± 3.74 MPa, with total-etch bonding type against tensile bond strength test is 15.83 ± 1.51 - 20.80 ± 3.95 MPa; with selfetch bonding type against shear bond strength test is 6.7 - 25.32 ± 4.91 MPa; and with total etch is 13.88 ± 5.50 - 30.25 ± 7.00 MPa.