Pengaruh nanofilled resin coating terhadap kekuatan tarik diametrikal dan daya serap air semen ionomer kaca (laporan penelitian)

1.0


Oleh : Willy Chan

Info Katalog

Nomor Panggil : 617.695 CHA p

Penerbit : FKG - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2019

Pembimbing 1 : drg. Rosalina Tjandrawinata, M.Si., Ph.D.

Subyek : Dental materials;Glass Ionomer Cements

Kata Kunci : diametral tensile strength, water sorption, nanofilled resin coating


File Repositori
No. Nama File Ukuran (KB) Status
1. 2019_TA_KG_040001500175_Halaman-Judul.pdf 834.07
2. 2019_TA_KG_040001500175_Bab-1.pdf 581.03
3. 2019_TA_KG_040001500175_Bab-2.pdf 810.48
4. 2019_TA_KG_040001500175_Bab-3.pdf 654.9
5. 2019_TA_KG_040001500175_Bab-4.pdf 989.56
6. 2019_TA_KG_040001500175_Bab-5.pdf 616.95
7. 2019_TA_KG_040001500175_Bab-6.pdf 658.37
8. 2019_TA_KG_040001500175_Bab-7.pdf 576.4
9. 2019_TA_KG_040001500175_Daftar-pustaka.pdf 662.97
10. 2019_TA_KG_040001500175_Lampiran.pdf 3141.25

S Semen Ionomer Kaca (SIK) merupakan suatu bahan tumpatan yang berikatandengan dentin dan email secara kimiawi dan banyak dipakai di kedokteran gigi.SIK memiliki biokompatibilitas yang baik terhadap jaringan gigi dan jugamelepaskan fluorida sehingga membuat gigi terhindar dari karies. Pada penelitianini digunakan SIK tipe 2 (EQUIA Forte , GC. Japan) yang dimanipulasi secaramekanik. Sampel SIK dimasukkan ke dalam cetakan yang menghasilkan sampelberdiameter 6,00,3 mm dan tinggi 3,00,2 mm dibagi menjadi 2 kelompok.Sepuluh sampel SIK yang tidak diaplikasikan nanofilled resin coating sebagaikelompok kontrol dan 10 sampel SIK yang diaplikasikan nanofilled resin coatingsebagai kelompok perlakuan. Sampel akan diinkubasi selama 24 jam denganmesin inkubator dengan suhu 37oC. Uji t tidak berpasangan menunjukkanperbedaan bermakna (p<0,05) pada kekuatan tarik diametrikal SIK kelompokperlakuan baik sampel immediate (6,99  0,76 MPa) maupun sampel 24 jam (7,85 1,28 MPa) dibandingkan kelompok kelompok kontrol immediate (5,06  0,70MPa) maupun 24jam (6,09  0,82 MPa). Uji statistik yang sama menunjukkantidak ada perbedaan yang signifikan pada daya serap SIK pada kelompokperlakuan. Disimpulkan aplikasi nanofilled resin coating meningkatkan kekuatantarik diametrikal pada sampel immediate dan peningkatan yang lebih tinggi padasampel 24 jam.

G Glass Ionomer Cement (GIC) is a material widely used in dentistry that binds todentine and enamel chemically. GIC has good biocompatibility with dental tissuesand also releases fluoride to make tooth immune of caries. In this study we usedtype 2 GIC (EQUIA Forte , GC. Japan) which was mechanically manipulated.The GIC mixture were inserted into a mold which produced a sample of 6.00.3mm in diameter and 0.30.2 mm in height, divided into 2 groups. Ten GICsamples were not applied with nanofilled resin coating as the control group andten GIC samples were applied with nanofilled resin coating as the treatmentgroup. The samples were incubated at 37oC for 24 hours. The unpaired t testshowed a significant difference (p<0.05) in the diametral tensile strength of GICin the treatment group both in the immediate samples (6.99  0.76 MPa) and inthe 24-hour samples (7.85  1.28 MPa) compared to the immediate controlsamples (5,06  0,70 MPa) and 24-hour control sample (6.09  0.82 MPa). Thesame statistical test showed no significant difference in the water sorption of GICin the treatment group. It can be concluded, the application of nanofilled resincoating provided an increase in diametral tensile strength in the immediatesamples and higher in 24 hours.