Pengaruh konsentrasi 5% air klorin terhadap kekasaran permukaan resin komposit nanofil (Laporan Penelitian)


Oleh : Muhammad Qadri Ramadhan

Info Katalog

Nomor Panggil : 617.634 2 RAM p

Penerbit : FKG - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2020

Pembimbing 1 : drg. Wiena Widyastuti, Sp.KG(K)

Subyek : Endodontics

Kata Kunci : chlorinated water, nanofilled composite resin, surface roughness


File Repositori
No. Nama File Ukuran (KB) Status
1. 2020_TA_KG_040001600091_Halaman-Judul.pdf 438.65
2. 2020_TA_KG_040001600091_Lembar-Pengesahan.pdf 902.4
3. 2020_TA_KG_040001600091_BAB-1_Pendahuluan.pdf 182.68
4. 2020_TA_KG_040001600091_BAB-2_Tinjauan-Pustaka.pdf 422.68
5. 2020_TA_KG_040001600091_BAB-3_Kerangka-Teori,-Kerangka-Konsep,-dan-Hipotesis.pdf 169.92
6. 2020_TA_KG_040001600091_BAB-4_Metode-Penelitian.pdf 996.41
7. 2020_TA_KG_040001600091_BAB-5_Hasil-Penelitian.pdf 249.73
8. 2020_TA_KG_040001600091_BAB-6_Pembahasan.pdf 214.09
9. 2020_TA_KG_040001600091_BAB-7_Kesimpulan-dan-Saran.pdf 87.22
10. 2020_TA_KG_040001600091_Daftar-Pustaka.pdf 217.08
11. 2020_TA_KG_040001600091_Lampiran.pdf 3002.98

L Latar belakang: Klorin merupakan kandungan yang umum digunakan sebagaidesinfektan yang berfungsi untuk mengurangi jumlah bakteri dan mikroorgsanismedi dalam air. Air kolam renang dapat menjadi asam apabila kandungan klorinmemiliki pH kurang dari 7. Resin komposit yang terpapar air dengan sifat asamdapat menyebabkan degradasi matriks pada permukaan restorasi, sehingga dapatmenyebabkan kekasaran permukaan resin komposit. Tujuan: Untuk mengetahuipengaruh air klorin terhadap kekasaran permukaan resin komposit nanofil. Metode:Sampel yang digunakan adalah resin komposit nanofil berbentuk silinder dengandiameter 10 mm dan tinggi 2 mm yang direndam kedalam 10 mL air klorin. Sampeldirendam dan disimpan di ice cube tray. Air klorin dibuat dengan menambahkan0,05 gr klorin pada 100 mL air. Air diganti setiap 24 jam. Sampel diukur sebelumperendaman, hari ke-3, ke-5, dan ke-10 dengan alat surface roughness tester. Hasil:Adanya peningkatan kekasaran permukaan sampel resin komposit setelah direndampada air klorin. Pada uji normalitas menunjukkan bahwa data terdistribusi normal(p>0,05). Uji ANOVA repeated menunjukkan adanya perbedaan signifikan(p<0,05). Kesimpulan: Terdapat pengaruh klorin pada air klorin terhadapkekasaran permukaan resin komposit nanofil.

B Background: Chlorine is one of the substances that is commonly used as adisinfectant that works to reduce the bacteria and microorganism in the water. Thewater is acidic if the pH of chlorine is below 7. Composite resin that is exposed toacidic water can cause matrix degradation on the restoration surface. Aim: The aimof this study is to determine the effect of chlorine in swimming pool water on thesurface roughness of nanofilled composite resin. Method: The sample is acylindrical nanofilled composite resin with 10 mm diameter and 2 mm height thatis immersed in 10 mL chlorinated water. Samples are immersed and stored in anice cube tray. The water is made by added 0.05 grams of chlorine to 100 mL ofwater. The water is replaced every 24 hours. Samples is measured beforeimmersion, day-3, day-5, and day-10 of immersion with surface roughness tester.Result: There is a significant increase of surface roughness after being immersedin chlorinated water. Normality test showed that the data were normally distributed(p>0.05). Repeated ANOVA test showed a significant difference (p<0.05).Conclusion: This study was proven that there is an effect of submersion ofchlorinated water on nanofilled composite resin surface roughness.